Jon_Beveryman t1_je7oxqk wrote

Reply to comment by wwjgd27 in Does the metal in the solid core of a rocky planet have any special properties? by VillagerNo4

No, they're not the same. The (111) plane in FCC and the (1000) plane in HCP are equivalent but if you look down the [111] and [1000] directions you will see that the stacking sequence is different. This is usually described as ABCABC (FCC) vs ABAB (HCP). This is, for instance, why you can have FCC <--> HCP phase transformations produced solely by stacking faults.

1

wwjgd27 t1_je8nghy wrote

I thought ABAB stacking was for graphite and other graphitic structures since each stack of graphene is missing a carbon atom at the center of the hexagonal rings which would give it the symmetry allowing for ABCABC stacking in both HCP (0001) planes and FCC (111) planes? Interesting conversation by the way!

1